T209 Wear resistant polyurea coating
| Payment Type: | L/C,T/T,Western Union |
|---|---|
| Incoterm: | FOB,CIF |
| Min. Order: | 800 Kilometer |
| Delivery Time: | 12 Days |
| Packaging: | Component A: 20KG/barrel Component B: 10KG/barrel |
|---|---|
| Productivity: | 1000000KG/month |
| Brand: | UMSN |
| Transportation: | Ocean,Land |
| Place of Origin: | GUANGNDONG |
| Supply Ability: | 100000KG/month |
| Certificate: | ISO9001 |
| HS Code: | 3209100000 |
| Port: | XIANMEN,GUANGZHOU,SHENZHEN |
Basic Info
Model No.: T209
Product Description
T209 Wear resistant polyurea coating
Product introduction polyaspartic polyurea
The component A is composed of an aliphatic polyurea modified resin, a pigment filler, an auxiliary agent, and the like, and the component B is composed of an aliphatic isocyanate. It can be hand-painted, rolled and high-pressure without spraying. The construction process has extremely low VOC emissions and is in line with national environmental protection policies. polyaspartic vs polyurea
Performance characteristics polyaspartic coating
Excellent UV resistance, high elasticity, strong resistance to stone and sand impact, and good adhesion to various substrates. Suitable for weathering finishes and floor wear finishes for Wind Turbine Blades.
| Technical Performance | Quick Information | ||
| Adhesion | ≥10.0MPa | Density (film) | Component A: 1.5-1.55 Component B: 1.05 Mixing: 1.3-1.35 |
| Tensile Strength | ≥10MPa | Solid Content (%) | 90% |
| Elongation at Break | ≥50% | Construction Period(25℃) | 30-60min |
| Flexibility | ≤1mm | Dry Film Thickness | 100-500µm |
| Impact Resistance | ≥50kg.cm | Theoretical Coverage | 0.2kg/m² (when dry film is 150µm) |
| Low Temperature Bending | -40℃ | Surface Drying | 1-2h |
| Wear Resistance (750g/500r) | ≤0.04g | Actual Drying | 24h |
| Water Resistance 30days | No corrosion, No bubble, No shedding | Re-coat Time | 24-48h |
| Acid Resistance 240h (5% H₂SO₄) | No corrosion, No bubble, No shedding | Construction Methods | Brush, roller, airless spraying, spraying |
| Alkali Resistance 240h (5%NaOH) | No corrosion, No bubble, No shedding | | |
| Salt Resistance 240h (3%NaCl) | No corrosion, No bubble, No shedding | | |
| Oil Resistance 240h | No corrosion, No bubble, No shedding | | |
| Water resistance 240h | No corrosion, No bubble, No shedding | | |
| UV resistant 1500h | No discoloration, No bubble, No shedding | | |
Polyurea Polyaspartic Mixing: Waterproof coating: curing agent=1:1 (please see label notice)
Shelf Life: coating component for 12moths, curing agent for 6 mothsThe polyurea A component is 12 months, and the curing agent component B is 12 months (the product expires and the test can still be used).
Package: Polyurea coating : 20kg Curing agent : 10kg
Polyaspartic coatings, We offer a mini sample kit and a money back guarantee.
Contact us if you need more details on T209 Wear Resistant Coating. We are ready to answer your questions on packaging, logistics, certification or any other aspects about T209 Polyurea Coating、Wear Resistant Polyurea Coating. If these products fail to match your need, please contact us and we would like to provide relevant information.
Product Categories : Polyurea Waterproofing > UMS-AUPT Polyurea System